How to weld stainless steel sheets? The welder has to learn

Characteristics of argon arc welding of stainless steel sheets
(1) The stainless steel sheet has poor thermal conductivity and is easily burned directly.
(2) No welding wire is required for welding, and the base metal is directly fused.
Therefore, the quality of stainless steel sheet welding is closely related to the operator, equipment, materials, construction methods, external environment during welding and testing.
In the welding process of stainless steel sheets, no welding consumables are required, but the following materials are required to be relatively high:
First, the purity, flow rate and argon time of argon gas,
Second, the tungsten electrode, a good tungsten electrode has a crucial impact on the welding results.

如何焊接不锈钢薄板?焊工不得不学的知识

不锈钢薄板的氩弧焊焊接特点
(1)不锈钢薄板的导热性差,容易直接烧穿。
(2)焊接时不需要焊丝,母材直接熔合。
因此,不锈钢薄板焊接的质量与操作者、设备、材料、施工方法、焊接时的外部环境及检测等因素息息相关。
在不锈钢薄板的焊接过程中,不需要焊材,但是对以下材料要求比较高:
一是,氩气的纯度、流量大小及通氩时间,
二是,钨极,一根好的钨极对焊接结果有着至关重要的影响。
(1)氩气
氩气的纯度必须大于99.99%以上。氩气主要是对熔池进行有效的保护,在焊接过程中防止空气对熔池侵蚀而引起氧化,同时对焊缝区域进行有效的空气隔离,使焊缝区域得到保护,提高焊接性能。
(2)钨极
钨极表面要光滑,端部一定要磨尖,且同心度好。这样焊接时高频引弧好、电弧稳定性好,熔深深,熔池能保持稳定,焊缝成形好,焊接质量好。如果钨极表面烧坏或表面有污染物、裂纹、缩孔等缺陷时,这样焊接时高频引弧困难,电弧不稳定,电弧有漂移现象,熔池分散,表面扩大,熔深浅,焊缝成形差,焊接质量差。
结论
(1)钨极氩弧焊稳定性好,不同钨极形状对不锈钢薄板焊接质量有较大影响。
(2)平顶锥端头钨极焊接可提高单面焊双面成形率,减小焊接热影响区,焊缝成形美观,综合力学性能较好。
(3)采用正确的焊接方法可有效预防焊接缺陷。

 